Factory Price Fireclay Refractory Castable High Alumina Castable
♦High refractoriness, high refractoriness under load.
♦High density, low porosity.
♦Good slag resistance and corrosion resistance.
♦High strength and wear resistance.
♦Good resistance to flake performance.
♦Good thermal shock stability.
♦Scouring resistance
♦Good hot strength.
Application：
♦In construction concretes, rapid strength development is achieved, even at low temperatures.
♦In construction concretes, high chemical resistance is possible.
♦In refractory concretes, strength is maintained at high temperatures.
♦As a component in blended cement formulations, various properties such as ultra-rapid strength development and controlled expansion can be obtained.
| Product | CA-65 | CA-68 | CA-70 | CA-75 | CA-80 | |
| Chemical Composition (%) | Al2O3 | 64-66 | 67-69 | 69-71 | 73-75 | 77-80 |
| CaO | 32-34 | 29-31 | 27-29 | 23-25 | 18-20 | |
| SiO2 | 1.8 | 1.2 | 0.3 | 0.3 | 0.3 | |
| Fe2O3 | 0.6 | 0.6 | 0.3 | 0.3 | 0.3 | |
| Specific Surface (cm2/g) | 4500 | 4500 | 5000 | 5500 | 7000 | |
| Setting time (h:min) | Initial setting (min) | 0:40 | 0:40 | 0:40 | 0:45 | 0:45 |
| Final Setting (min) | 8:00 | 8:00 | 10:00 | 10:00 | 10:00 | |
| Cold Modulus of Rupture (MPa) | 24 hour | 6.0min | 6.0min | 6.0min | 6.0min | 5.0min |
| 72 hour | 8.0min | 8.0min | 8.0min | 8.0min | 6.0min | |
| Cold Crushing Strength (Mpa) | 24hour | 45.0min | 45.0min | 45.0min | 45.0min | 35.0min |
| 72hour | 70.0min | 70.0min | 70.0min | 70.0min | 60.0min | |
| Refractoriness (°C) | 1680 | 1710 | 1730 | 1750 | 1770 | |