The zirconium mullite brick produced by our company is made of mullite as aggregate and zircon as raw material. After kneading, molding and drying, it is fired at high temperature in the shuttle kiln.
The brick has a dense crystal structure, high bulk density, large volume, high mechanical strength at normal temperature and high temperature, good thermal shock stability, low reburning shrinkage and high temperature creep, and high chemical stability and alkali resistance. Characteristics such as erosion.
Zirconium mullite bricks are mainly used in large glass kiln melting pools, picture tube kiln furnaces, regenerator partition walls and chemical and metallurgical industrial furnaces.
The dimensions, physical and chemical indicators and service life our products have reached or exceeded the level of similar products in domestic and abroad.
Technical Parameter of Zircon Mullite Bricks:
| Item | Zircon Mullite Brick | |||||
| Chemical composition | Al2O3 | ≥70 | ≥59 | ≥57 | ≥47 | ≥72 |
| ZrO2 | ≥17 | ≥19.5 | ≥25.5 | ≥30 | ≥11 | |
| SiO2 | ≤12 | ≤20 | ≤14.5 | ≤20 | ≤12 | |
| Fe2O3 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.3 | ≤0.5 | |
| Apparent Porosity％ | ≤17 | ≤17 | ≤17 | ≤18 | ≤17 | |
| Bulk Density g/cm3 | ≥3.15 | ≥2.95 | ≥3.15 | ≥3.10 | ≥3.1 | |
| Cold Crushing Strength Mpa | ≥90 | ≥100 | ≥120 | ≥100 | ≥90 | |
| 0.1Mpa Refractoriness Under Load T0.6 ℃ | ≥1650 | ≥1650 | ≥1650 | ≥1650 | ≥1630 | |
| Permanent Linear Change On Reheating（%）1500℃X2h | ±0.3 | ±0.3 | ±0.3 | ±0.3 | ±0.3 | |
| 20-1000℃ Thermal Expansion % (x 10-6) | 0-0.6 | 0-0.6 | 0-0.6 | 0-0.6 | 0-0.6 | |
| Thermal Conductivity (Average800℃) W / (M.K) | ≤ 2.19 | ≤ 2.19 | ≤ 2.1 | ≤ 2.1 | ≤ 2.19 | |
| Pyrometric Cone Equivalent ℃ SK | 31 | 31 | 31 | 31 | 31 | |